Bambu Lab PLA Series - 1.75mm (with reel)
PLA is the most commonly used material in 3D printing because it is easy to print and inexpensive. At the same time, its stiffness and strength meet most printing needs. Bambu PLA Basic is designed specifically for high-speed printing. Compared to general-purpose PLA, it can easily achieve printing speeds of up to 250-300 mm/s, and has excellent toughness and Z-layer strength.
Eco-friendly
Bambu Lab spools reduce plastic waste by 20%.
RFID for smart printing
All printing parameters are embedded in RFID and can be read by Bambu Lab's AMS (Automated Material System) .
No more tedious adjustments needed for loading and printing!
Multiple colors
Bambu Lab PLA Basic is available in more than 5 colors to meet all your needs.
black
White
silver
red
blue
Tuozhu Green
yellow
orange color
off white
coffee brown
gold
Purple
Magenta
Please contact us for more details about Bambu Lab PLA and 3D printers !
| diameter | 1.75 mm |
| Net weight of wire | 1 kg |
| spool material | ABS (temperature resistant to 70°C ) |
| spool size | Diameter : 200 mm; Height: 67 mm |
| Pre- print drying settings | 55 °C, 8 hours |
| Printing and storing humidity | < 20% RH (sealed with desiccant) |
| Nozzle temperature | 190 - 230 ̊C |
| Printing plate type | Low temperature plate, high temperature plate or textured PEI plate |
| Printing plate preparation | 35 - 45 ̊C |
| Cooling fan | 100% |
| Printing speed | < 300 mm /s |
| Retraction length | 0.6 - 1.0 mm |
| Retraction speed | 20 - 40 mm /s |
| Internal temperature | 25 - 45 ̊C |
| Maximum overhang angle | 55 ̊C |
| Maximum bridging length | 30 mm |
| Supporting materials | Support PLA |
physical properties
| density | 1.24 g/cm³ |
| Vicat softening temperature | 57 ̊C |
| Heat distortion temperature | 57 ̊C |
| melting temperature | 160 ̊C |
| Melt Flow Index | 42.4 ± 3.5 g/10 min |
Mechanical properties
| Tensile strength | 39 ± 2 MPa |
| Elongation at break | 12.2 ± 0.4% |
| Flexural modulus | 2750 ± 60 MPa |
| Bending strength | 76 ± 3 MPa |
| Impact strength | 26.6 ± 2.8 kJ/ m² |