Bambu Lab PLA Matte Series
Regular price
¥3,400 JPY
Unit price
/
Unavailable
税込価格
日本国内VR実測事例の探索
Maker Faire 会場 3Dツアー
Galois P4で2026年9月5~6日に撮影したMaker Faire会場の3D空間をご覧いただけます。 会場全体を自由に移動しながら、高精細な空間モデルをご体験ください。
RepRap Festival 2026 - 3DMart
RepRap Festival 2026の会場をGalois P4で撮影しました。 会場内を自由に移動しながら、3DMartの展示内容と高精細な3D空間をご体験いただけます。
Bambu Lab PLA Matte Series - 1.75mm (with roll)
PLA Matte is the most commonly used material in 3D printing because it is easy to print and inexpensive. At the same time, its stiffness and strength meet most printing needs. Bambu PLA Matte is designed specifically for high-speed printing. Compared to general-purpose PLA from other brands, it can easily achieve printing speeds of up to 250-300 mm/s, and has excellent toughness and Z-layer strength.
Eco-friendly
Bambu Lab spools reduce plastic waste by 20%.
RFID for smart printing
All printing parameters are embedded in RFID and can be read by Bambu Lab's AMS (Automated Material System) .
No more tedious adjustments needed for loading and printing!
Finished product display:
Matte White
Matte carbon black
Matte Gray
Matte Lemon Yellow
Foliage Green
Matte Deep Blue
Matte Orange
Matte pink
Matte Purple
Matte Ice Blue
Matte Ocean Blue
Matte Red
Matte Dark Coffee
Printing Tips
The recommended drying conditions for PLA matte finishes are 8 hours at 55°C in an explosion drying oven, or 12 hours at 75°C on a printer's heated bed. For more information on wire drying, please refer to the WIKI.
Packaging contents
Wire *1 & Desiccant *1
Instruction manual *1 & spool sticker *1
Outer box *1
Cable label *1
| diameter | 1.75 mm |
| Net weight of wire | 1 kg |
| spool material | ABS (temperature resistant to 70°C ) |
| spool size | Diameter : 200 mm; Height: 67 mm |
| Pre- print drying settings | 55 °C, 8 hours |
| Printing and storing humidity | < 20% RH (sealed with desiccant) |
| Nozzle temperature | 190 - 230 ̊C |
| Printing plate type | Low temperature plate, high temperature plate or textured PEI plate |
| Printing plate preparation | 35 - 45 ̊C |
| Cooling fan | open |
| Printing speed | < 300 mm /s |
| Retraction length | 0.6 - 1.0 mm |
| Retraction speed | 20 - 40 mm /s |
| Internal temperature | 25 - 45 ̊C |
| Maximum overhang angle | 55 ̊C |
| Maximum bridging length | 30 mm |
| Supporting materials | Support PLA |
physical properties
| density | 1.31 g/cm³ |
| Vicat softening temperature | 63 ̊C |
| Heat distortion temperature | 57 ̊C |
| melting temperature | 160 ̊C |
| Melt Flow Index | 39.4 ± 3.2 g/min |
Mechanical properties
| Tensile strength | 30 ± 5 MPa |
| Elongation at break | 14.8 ± 4.2% |
| Flexural modulus | 2360 ± 250 MPa |
| Bending strength | 53 ± 6 MPa |
| Impact strength | 19.2 ± 3.7 kJ/ m² |