Bambu Lab PC Series - 1.75mm (with reel)
RFID for smart printing
All printing parameters are embedded in RFID and can be read by our AMS (Automated Material System). Load and print! No more tedious setup steps.
Print Tips
• Due to the transparent nature of the filament, laser extrusion calibration may be affected when printing on transparent PC.
• Bambu PC requires proper drying before printing. It is recommended to dry at 80 °C in a blower oven for 8 hours, or at 100 °C for 12 hours on the printer's heated bed.
Contents
1 spool & 1 desiccant
Instruction manual *1 & spool sticker *1
Outer packaging *1
Cable label *1
Features
• Excellent heat resistance
• Excellent mechanical properties
• High impact resistance and durability
• Suitable for engineering applications
• Equipped with high-temperature reusable spools
• Diameter: 1.75mm +/- 0.03mm
Please contact us for more details about Bambu Lab PLA and 3D printers !
| diameter | 1.75 mm |
| Net weight of wire | 1 kg |
| spool material | PC+ABS (temperature resistant to 90°C ) |
| spool size | Diameter : 200 mm; Height: 67 mm |
| Pre- print drying settings | 55 °C, 8 hours |
| Printing and storing humidity | < 20% RH (sealed with desiccant) |
| Nozzle temperature | 260 - 280 ̊C |
| Printing plate type | Low-temperature printing platform , high-temperature printing platform , or PEI texture platform |
| heated bed temperature | 90 - 110 ̊C |
| Cooling fan | 0 -60% |
| Printing speed | < 300 mm /s |
| Retraction length | 0.8 - 1.4 mm |
| Retraction speed | 20 - 40 mm /s |
| Internal temperature | 45 - 60 °C |
| Maximum overhang angle | ~70 ̊ |
| Maximum bridging length | ~40 mm |
physical properties
| density | 1.20 g/cm³ |
| Vicat softening temperature | 119 ̊C |
| Heat distortion temperature | 117 ̊C |
| melting temperature | 228 ̊C |
| Melt Flow Index | 32.2 ± 2.9 g/10 min |
Mechanical properties
| Tensile strength | 55 ± 4 MPa |
| Elongation at break | 3.8 ± 0.3% |
| Flexural modulus | 2310 ± 70 MPa |
| Bending strength | 108 ± 4 MPa |
| Impact strength | 34.8 ± 2.1 kJ/m² |