Bambu Lab PA6-CF Black
Bambu PA6-CF is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly high stiffness and strength properties in dry environments while maintaining excellent heat resistance and impact resistance. Similar to other Bambu CF filaments, these superior mechanical properties make it ideal for printing fixtures, jigs, automotive and mechanical parts, and a variety of structural and engineering components used in dry environments.
Exceptional strength and stiffness
As a new member of Bambu's high-performance wire family, PA6-CF maintains excellent stiffness and strength even in dry environments, making it ideal for printing load-bearing structural components.
| Normal PA-CF | PA6-CF | improve% | |
| Strength (flexural strength - XY, dry state) | 128MPa | 151MPa | 18% |
| Stiffness (flexural modulus - XY, dry state) | 4420MPa | 5460MPa | twenty four% |
Impact and vibration resistance
Bambu PA6-CF offers excellent shock resistance, ensuring your prints are effectively protected against vibration. It is typically used for printing models that need to withstand impacts, collisions, and vibrations.
* Prints from PA6-CF will harden if left in a humid environment for more than one day.
Excellent thermal resistance
| wire | PLA Basic | PETG Basic | ABS | ASA | PC | PA6-CF | PAHT-CF | PET-CF |
| Heat distortion temperature / ℃ (0.45 MPa) | 57℃ | 69℃ | 87℃ | 100℃ | 117℃ | 186℃ | 194℃ | 205℃ |
Parameter comparison
Learn more about the comparisons of different cables in the Bambu Cable Guide >>
| Ordinary PA6-CF | PA6-CF | PAHT-CF | |
| work | Nylon 6, carbon fiber | Nylon 6, carbon fiber | PA12 and other long-chain PA, carbon fiber |
| AMS compatibility | incompatible | incompatible | Compatible |
| Dry before use | Required | Required | Required |
| Printing speed | < 100 mm/s | < 100 mm/s | < 100 mm/s |
| Printer type | shell | shell | shell |
| Toughness (impact strength - XY, dry state) | 35.7 kJ/m² | 40.3 kJ/m² | 57.5 kJ/m² |
| Toughness (Impact Strength - XY, Wet State) | 65.4 kJ/m² | 57.2 kJ/m² | 62.3 kJ/m² |
| Strength (flexural strength - XY, dry state) | 141MPa |
| diameter | 1.75 mm |
| Net weight of wire | 500 g |
| spool material | PC+ABS (temperature resistant to 90°C ) |
| spool size | Diameter : 200 mm; Height: 67 mm |
| Pre- print drying settings | 80 °C, 8-12 hours X1 Series Printers Heated Bed: 90 - 100 °C, 12 h |
| Printing and storing humidity | < 20% RH (sealed with desiccant) |
| Nozzle temperature | 260 - 290 ̊C |
| Printing plate type | Engineering printing plates, high-temperature plates, or textured PEI plates |
| Printing plate preparation | 80 - 100 ̊C |
| Cooling fan | 0-60% |
| Printing speed | < 100 mm /s |
| Retraction length | 0.8 - 1.4 mm |
| Retraction speed | 20 - 40 mm /s |
| Internal temperature | 45 - 60 ̊C |
| Maximum overhang angle | ~70 ̊C |
| Maximum bridging length | ~40 mm |
| Supporting materials | Supports PA/PET |
physical properties
| density | 1.09 g/cm³ |
| Vicat softening temperature | 223 ̊C |
| Heat distortion temperature | 186 ̊C |
| melting temperature | 223 ̊C |
| Melt Flow Index | 6.8 ± 0.6 g/10 min |
Mechanical properties
| Tensile strength | 102 ± 7 MPa |
| Elongation at break | 5.8 ± 1.6% |
| Flexural modulus | 5460 ± 280 MPa |
| Bending strength | 151 ± 8 MPa |
| Impact strength | 40.3 ± 2.5 kJ/ m² |