Bambu Lab SAS-CF Series
Bambu ASA-CF is designed for harsh outdoor conditions, offering superior weather resistance and UV protection. It retains the advantages of ASA while incorporating carbon fiber for increased stiffness and dimensional stability.
This makes it an ideal choice for building large vehicles with high durability and precision in harsh environments.
Exceptional outdoor durability
Bambu ASA-CF is one of the top materials for outdoor use, offering excellent resistance to harsh weather and UV radiation.
It is reinforced with carbon fiber, making it ideal for manufacturing durable gardening tools, outdoor furniture, and protective housings for electronic devices.
Optimization was performed for large-scale models.
Bambu ASA-CF uses carbon fiber to reduce warping and ensure excellent dimensional stability, making it ideal for large models or parts that require high precision, such as parts in assembly.
Smooth matte finish
With its smooth, matte finish and minimal visible layer lines, Bambu ASA-CF boasts a refined, natural look, making it ideal for crafting intricate models such as flower pots and other outdoor decorations.
Enhance the rigidity of high load-bearing components
Bambu ASA-CF is 67% more rigid than standard ASA, making it the material of choice for components that need to withstand heavy loads and resist bending, such as camping accessories, plant stands, or other outdoor furniture.
| category | project | parameter |
|---|---|---|
| Recommended print settings | Drying settings | 80℃, 8 hours |
| Print humidity | < 20% RH (sealed, with desiccant) | |
| Nozzle temperature | 250 - 280 ℃ | |
| Bed temperature (including adhesive) | 80 - 100 ℃ | |
| Printing speed | < 250 mm/s | |
| Physical properties | density | 1.02 g/cm³ |
| softening temperature | 108 ℃ | |
| Heat distortion temperature | 110 ℃ | |
| melting temperature | 210 ℃ | |
| Melt Flow Index | 1.74 ± 0.3 g/10 minutes | |
| Mechanical properties | tensile strength | 34 ± 3 MPa |
| Elongation at break | 9.6 ± 1.4% | |
| Flexural modulus | 3740 ± 130 MPa | |
| Bending strength | 72 ± 5 MPa | |
| Impact strength | 14.0 ± 2.2 kJ/m² |