Bambu Lab ABS-GF Series
Bambu ABS-GF is a glass fiber reinforced ABS filament with improved mechanical properties and aesthetics.
Compared to regular ABS, ABS-GF is superior in strength, rigidity, high temperature resistance, and dimensional stability, while also being less prone to deformation and warping.
Fiberglass gives the product a smooth, matte finish with subtle shimmer, blurring the lines between the layers.
ABS-GF, with its inherent water resistance, abrasion resistance, durability, and vibrant colors, is an ideal choice for mechanical parts and decorative items.
Enhance strength and stiffness
ABS-GF has superior strength and stiffness compared to ordinary ABS, making it ideal for load-bearing and bending-resistant components.
Higher dimensional stability
Glass fiber reinforced materials give ABS-GF better dimensional stability than ordinary ABS, thereby minimizing warping and deformation during the printing process.
This makes it ideal for manufacturing complex mechanical assemblies or geometric components.
Refined matte finish
The seamless matte surface and virtually invisible layer lines give ABS-GF a smooth appearance, making it ideal for decorative and fine-grained parts.
Waterproof and durable
Bambu ABS-GF offers enhanced water resistance and durability, making it ideal for printing durable production and household items such as machine housings, connectors, and molds.
RFID Smart Printing
All printing parameters are embedded in RFID tags and can be read through our AMS (Automated Material System).
Load and print! No complicated setup steps required.
| category | project | parameter |
|---|---|---|
| Recommended print settings | Drying settings | 80℃, 8 hours |
| Print humidity | < 20% RH (sealed, with desiccant) | |
| Nozzle temperature | 240 - 270 ℃ | |
| Bed temperature (including adhesive) | 80 - 100 ℃ | |
| Printing speed | < 180 mm/s | |
| Physical properties | density | 1.08 g/cm³ |
| softening temperature | 103 ℃ | |
| Heat distortion temperature | 99 ℃ | |
| melting temperature | 202 ℃ | |
| Melt Flow Index | 7.56 ± 1.4 g/10 minutes | |
| Mechanical properties | tensile strength | 36 ± 3 MPa |
| Elongation at break | 6.3% ± 1.2% | |
| Flexural modulus | 2860 ± 130 MPa | |
| Bending strength | 68 ± 4 MPa | |
| Impact strength | 14.5 ± 1.5 kJ/m² |